Nanostructure Formation Leading To Modify the Optical Absorption of Gaq3 Thin Films
Article Sidebar
Main Article Content
Abstract
This paper reports on the preparation of nanostructure along tris(8-hydroxyquinoline) gallium, Gaq3 thin film aiming at modifying its optical absorption property. The formation of nanostructure was achieved by means of thermal annealing in the temperature range from 85 oC to 255 oC under a flowing nitrogen gas for 10 minute. The results showed a modified optical absorption at 235 oC to produce a broad absorption spectrum which is quite wider than that of pristine film. It was noticed from the results of x-ray diffraction, XRD and field emission scanning electron microscopy, FESEM techniques that such annealing process has led to the formation of amorphous nanorods at specific temperatures, thereby modulating the films optical absorption. The relatively decreased absorption intensity at 255 oC was attributed to the partial crystalline formation and degraded nanostructures due to hard heating. Finally, the nanostructure growth was seen to possess a unique feature in modifying the optical behaviours of the Gaq3 thin films.
Downloads
Article Details
Section
This work is licensed under a Creative Commons Attribution 4.0 International License.
Authors who publish with this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License [CC BY-NC-SA 4.0] that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work, with an acknowledgment of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online.